US Units (English) | SI Units (Metric) |
|
Tensile strength | 600 Ksi | 4137 MPa |
Tensile modulus | 35 Msi | 242 GPa |
Elongation | 1.5% | 1.5% |
Density | 0.065 lb/in3 | 1.81 g/cm3 |
Filament Diameter | 0.283 mils | 7.2 μm |
Yield | 400 ft/lb | 270 m/kg |
Unidry® fabrics can be produced from DowAksa, Toray or Zoltek fibers, according to customer request.
FABRIC PROPERTIES:
US Units (English) | SI Units (Metric) |
|
Area weight | 5.90 oz/yd2 (+0.06oz/yd2) | 200 g/m2 (+ 2 g/m2) |
Standard production widths | 19.69 in (± 0.1181 in) 23.62 in (± 0.1181 in) 39.37 in (± 0.1181 in) 50.00 in (± 0.1181 in) 70.87 in (± 0.1181 in) |
500 mm (± 3 mm) 600 mm (± 3 mm) 1000 mm (± 3 mm) 1270 mm (± 3 mm) 1800 mm (± 3 mm) |
Maximum production width | 70.87 in (± 0.1181 in) | 1800 mm (± 3 mm) |
Laminate thickness | 0.00787 in (± 2.5 %) | 0.2 mm (± 2.5 %) |
Bonding lay (76 dtex polyester scrim on 1 or 2 sides to keep together the carbon structure) |
0.10 oz/yd2 | 3.5 g/m2 |
Core diameter | 5.906 in | 150 mm |
Resin system compatibility |
Epoxy Phenolic Polyester Vinyl BMI |
* Unidry® ribbon of 600 mm width could be divided into 2-6 parts (with gaps between).